DemonTrich
- 6,394
- 313
Haters will hate.
No we'e All tired of seeing 10 diamond threads daily.
Enough
Last warning
Haters will hate.
O trust me lil grasshopper I don't hate, just call out BS when I see it is all. Happy Growing
Pressure vessel? All I am seeing is a mason jar... lol where's the prv? A pressurized vessel or "diamond miner" is just stainless steel, tri clamps, a port (for nitrogen injection to build pressure), sight glass, prv all pressure tested. This is just one method of several. Already told you a couple other methods on the other thread. Really don't think you have enough of the right equipment to make halfway decent sauce though. Getting down to -70 and sustaining that temp for your solvent and column isn't very feasible while open blasting, doubt you have a chiller. All this talk of open blasting, I kind of want to try now, see what I can do open blasting instead of using my cls and chiller, Would be a fun challenge I think. I know the quality just wont come close but i have some ideas on a good method of choice.Pour off into s pressure vessels add time...and diamonds
Im gonna make so many diamond threads... Its gonna be epicNo we'e All tired of seeing 10 diamond threads daily.
Enough
Last warning
Kick his ass C Bass!I'e mentioned it in tour very 1st "diamond" thread, that those are NOT diamonds.
2 reasons why I close tour threads.
1 duplicate threads for the same top s is not allowed.
2 posting things that are not true. I.e. your "diamonds. They are in fact not true actual diamonds. And I, and the rest of the community, do not want to learn misinformation on how to do or make something.
And thanks again for NOT making yet another damn diamond thread. Diamonds are what' on my wife's finger (2ct actually). You have sauce in your jars, not sparkly, solid shards of diamonds.
Sounds like you found a good recrystillazation method. Pics?With the second batch I have been cryo temp cycling. 2 days cryo, 1 day heat, 1 day cryo..today is the last day of cryo then all heat at 90 degrees or so. The temp cycling has caused abundant cyrstallization on the bottom and sides. I hope I am doing this correct.